Liquid crystalline medium

ABSTRACT

The invention relates to a liquid-crystalline medium based on a mixture of polar compounds having negative dielectric anisotropy, which contains at least one compound of the formula I 
     
       
         
         
             
             
         
       
     
     and at least one compound of the formula II 
     
       
         
         
             
             
         
       
     
     in which
 
R 1 , R 2 , R 3 , R 4 , ring A, Z 1 , Z 2  and m are as defined in Claim  1,  
 
and to the use thereof for an active-matrix display based on the ECB, VA, PS-VA, FFS, PALO or IPS effect.

The invention relates to a liquid-crystalline medium based on a mixture of polar compounds having negative dielectric anisotropy, which contains at least one compound of the formula I and at least one compound of formula II

wherein

-   R¹ to R⁴ are each independently alkyl or alkoxy with 1 to 8 C atoms,     wherein one or more CH₂-groups are optionally replaced by —CH═CH—,     —CF₂O, or —O— in a way that —O— atoms are not linked directly to one     another,

-   X¹ and X² are each independently F, C₁ or CF₃, -   Z¹ and Z² are each independently a single bond, —CH₂CH₂—, —CH₂O—,     —OCH₂—, —CF₂O—, —OCF₂—, —COO— -   m is 0 or 1.

Media of this type are to be used, in particular, for electrooptical displays with active-matrix addressing based on the ECB effect, for IPS (in plane switching) and for FF5 (fringe field switching) displays.

The principle of electrically controlled birefringence, the ECB (electrically controlled birefringence) effect or DAP (deformation of aligned phases) effect was described for the first time in 1971 (M. F. Schieckel and K. Fahrenschon, “Deformation of nematic liquid crystals with vertical orientation in electrical fields”, Appl. Phys. Lett. 19 (1971), 3912). Papers by J. F. Kahn (Appl. Phys. Lett. 20 (1972), 1193) and G. Labrunie and J. Robert (J. Appl. Phys. 44 (1973), 4869) followed.

The papers by J. Robert and F. Clerc (SID 80 Digest Techn. Papers (1980), 30), J. Duchene (Displays 7 (1986), 3) and H. Schad (SID 82 Digest Techn. Papers (1982), 244) have shown that liquid-crystalline phases must have high values for the ratio between the elastic constants K₃/K₁, high values for the optical anisotropy Δn and values for the dielectric anisotropy Δ∈ of −0.5 to −5 in order to be suitable for use in high-information display elements based on the ECB effect. Electra-optical display elements based on the ECB effect have a homeotropic edge alignment. Dielectrically negative liquid-crystal media can also be used in displays which use the so-called IPS effect.

Industrial application of this effect in electro-optical display elements requires LC phases which have to satisfy a multiplicity of requirements. Particularly important here are chemical resistance to moisture, air and physical influences, such as heat, radiation in the infrared, visible and ultraviolet regions, and direct and alternating electric fields.

Furthermore, LC phases which can be used industrially are required to have a liquid-crystalline mesophase in a suitable temperature range and low viscosity.

None of the series of compounds having a liquid-crystalline mesophase that have been disclosed hitherto includes a single compound which meets all these requirements. Mixtures of two to 25, preferably three to 18, compounds are therefore generally prepared in order to obtain substances which can be used as LC phases. However, it has not been possible to prepare optimum phases easily in this manner, since no liquid-crystal materials having significantly negative dielectric anisotropy and adequate long-term stability have hitherto been available.

Matrix liquid-crystal displays (MLC displays) are known. Non-linear elements which can be used for individual switching of the individual pixels are, for example, active elements (i.e. transistors). The term “active matrix” is then used, where a distinction can be made between two types:

-   1. MOS (metal oxide semiconductor) transistors on a silicon wafer as     substrate. -   2. Thin-film transistors (TFTs) on a glass plate as substrate.

In type 1, the electro-optical effect used is usually dynamic scattering or the guest-host effect. The use of single-crystal silicon as substrate material restricts the display size, since even modular assembly of various part-displays results in problems at the joins.

In the case of the more promising type 2, which is preferred, the electro-optical effect used is usually the TN effect.

A distinction is made between two technologies: TFTs comprising compound semiconductors, such as, for example, CdSe, or TFTs based on polycrystalline or amorphous silicon. The latter technology is being worked on intensively worldwide.

The TFT matrix is applied to the inside of one glass plate of the display, while the other glass plate carries the transparent counterelectrode on its inside. Compared with the size of the pixel electrode, the TFT is very small and has virtually no adverse effect on the image. This technology can also be extended to fully colour-compatible displays, in which a mosaic of red, green and blue filters is arranged in such a way that a filter element is opposite each switchable pixel.

The TFT displays disclosed hitherto usually operate as TN cells with crossed polarisers in transmission and are back-lit.

The term MLC displays here covers any matrix display with integrated non-linear elements, i.e. besides the active matrix, also displays with passive elements, such as varistors or diodes (MIM=metal-insulator-metal).

MLC displays of this type are particularly suitable for TV applications (for example pocket TVs) or for high-information displays in automobile or aircraft construction. Besides problems regarding the angle dependence of the contrast and the response times, difficulties also arise in MLC displays due to insufficiently high specific resistance of the liquid-crystal mixtures [TOGASHI, S., SEKIGUCHI, K., TANABE, H., YAMAMOTO, E., SORIMACHI, K., TAJIMA, E., WATANABE, H., SHIMIZU, H., Proc. Euro-display 84, September 1984: A 210-288 Matrix LCD Controlled by Double Stage Diode Rings, pp. 141 ff., Paris; STROMER, M., Proc. Eurodisplay 84, September 1984: Design of Thin Film Transistors for Matrix Addressing of Television Liquid Crystal Displays, pp. 145 ff., Paris]. With decreasing resistance, the contrast of an MLC display deteriorates. Since the specific resistance of the liquid-crystal mixture generally drops over the life of an MLC display owing to interaction with the inside surfaces of the display, a high (initial) resistance is very important for displays that have to have acceptable resistance values over a long operating period.

The disadvantage of the MLC-TN displays disclosed hitherto is due to their comparatively low contrast, the relatively high viewing-angle dependence and the difficulty of producing grey shades in these displays.

There thus continues to be a great demand for MLC displays having very high specific resistance at the same time as a wide operating-temperature range, short response times and low threshold voltage with the aid of which various grey shades can be produced.

The invention has the object of providing MLC displays which are based on the ECB, VA (vertical alignment), PS-VA (polymer stabilized-VA), IPS or FPS effect and do not have the disadvantages indicated above, or only do so to a lesser extent, and at the same time have very high specific resistance values.

It has now been found that this object can be achieved if nematic liquid-crystalline mixtures which contain at least one compound of the formula I and at least one compound of the formula II are used in these display elements.

The invention thus relates to a liquid-crystalline medium having negative dielectric anisotropy which contains at least one compound of the formula I and at least one compound of the formula II.

LC compositions containing compounds of the formula I are known from U.S. 2008/0011984A1.

Preferred embodiments of the LC media are the following:

-   a) R¹, R², R³ and R⁴ are independently of each other preferably     alkyl, alkoxy or alkenyl. Alkyl and alkoxy are in each case a     straight chained residue containing 1 to 6 C atoms. The term     “alkenyl” comprises straight-chain and branched alkenyl groups with     2 to 7 C atoms. Straight-chain alkenyl groups are preferred. Further     preferred alkenyl groups are C₂-C₇-1E-alkenyl, C₄-C₇-3E-alkenyl,     C₅-C₇-4-alkenyl, C₆-C₇-5-alkenyl and C₇-6-alkenyl, in particular     C₂-C₇-1E-alkenyl, C₄-C₇-3E-alkenyl and C₅-C₇-4-alkenyl. Of these,     especially preferred alkenyl groups are vinyl, 1E-propenyl,     1E-butenyl, 1E-pentenyl, 1E-hexenyl, 1E-heptenyl, 3-butenyl,     3E-pentenyl, 3E-hexenyl, 3E-heptenyl, 4-pentenyl, 4Z-hexenyl,     4E-hexenyl, 4Z-heptenyl, 5-hexenyl and 6-heptenyl. Alkenyl groups     with up to 5 C atoms are particularly preferred. -   b) The compounds of formula I are selected from the following     formulae,

-   -   wherein “alkyl” and “alkyl*” independently of each other denote         C₁₋₆-alkyl and “alkenyl” and “alkenyl*” independently of each         other denote C₂₋₇-alkenyl. Especially preferred are LC media         containing one or more, preferably one, two or three compounds         of formula Ia preferably

-   c) The compounds of formula II are selected from the following     formulae IIa to IIr

-   -   wherein “alkyl” and “alkyl*” denote independently of each other         C₁₋₆-alkyl, “Alkenyl” denotes straight-chain alkenyl with 2 to 6         carbon atoms, preferably vinyl, CH₃CH═CH, CH₂═CHCH₂CH₂ and         CH₃CH═CHCH₂CH₂. Especially preferred LC media contain at least         one compound selected from the group of compounds of the formula         IIa, IIb, IId, IIf and IIi.     -   In the compounds of the formula II and the subformulae IIa to         IIr X¹ and X² denote preferably F and Cl. Especially preferred         are compounds wherein X¹═X²═F or X¹=Cl and X²═F. In a preferred         embodiment is X¹═X²═F.

-   d) The LC medium additionally contains one or more compounds     selected of formula III,

-   -   wherein     -   R⁵ and R⁶ are independently of each other alkyl or alkoxy with 1         to 8 C atoms wherein one or more CH₂-groups are optionally         replaced by —CH═CH—,

are independently of each other

-   -   n is 0 or 1.     -   The compounds of formula III are selected from the subformulae         IIIa to IIIn

-   -   in which     -   alkyl and     -   alkyl* each, independently of one another, denote a         straight-chain alkyl radical having 1-6 C atoms, and     -   alkenyl and     -   alkenyl* each, independently of one another, denote a         straight-chain alkenyl radical having 2-6 C atoms.     -   The medium according to the invention preferably contains at         least one compound of the formula IIIa, formula IIIb, formula         IIIe, IIIg, IIIh, and/or IIIi. Especially preferred is the         compound of the formula IIIi. Preferred mixtures contain the         compound of the formula IIIi in amounts of 5-25% by weight based         on the total mixture.     -   Particularly preferred compounds of the formulae IIIe and IIIf         are indicated below:

-   -   Especially preferred are LC mixtures which contain >30% by         weight, most preferred ≧35% by weight of at least one compound         of the formula

-   -   Preferred compounds of the formulae IIIh are indicated below:

-   f) Liquid-crystalline medium which additionally contains one or more     tetracyclic compounds of the formulae

-   -   in which     -   R⁷ and R⁸ each, independently of one another, have one of the         meaning indicated for R¹ in claim 1, and     -   w and x each, independently of one another, denote 1 to 6.

-   g) Liquid-crystalline medium which contains one or more compounds of     the formulae Z-1 to Z-15

-   -   in which R¹³-R²⁸ each, independently of one another, have the         meanings indicated for R¹, and z and m each, independently of         one another, denote 1-6. R^(E) denotes H, CH₃, C₂H₅ or n-C₃H₇.     -   Especially preferred is the compound of the formula Z-15.         Preferred LC mixtures contain 5-25% by weight of the compound of         the formula Z-15 based on the total mixture.

-   h) Liquid-crystalline medium which additionally contains one or more     biphenyl or terphenyl compounds of the formulae T-1 and B-1

-   -   in which R denotes alkyl, alkenyl, alkoxy, alkylalkoxy or         alkenyloxy having 1 or 2 to 6 C atoms, and alkenyl has the         meaning indicated above.     -   A preferred compound of the formula B-1 is a compound of the         formula B-1a

-   -   LC mixtures containing 5-25% by weight of at least one compound         of the formula T-1 and/or B-1 are preferred.

-   i) Liquid-crystalline medium which contains at least one compound     with a positive delta epsilon (As) selected from the formulae P-1 to     P-6,

-   -   in which R^(1*) has the meaning of R¹ in claim 1 and in L^(1*)         and L^(2*) each independently of one another denote H or F.     -   Particularly preferred media contain one or more compounds         selected from the compounds of the formulae P-1 to P-6 wherein         L¹ and L^(2*) are both F.     -   Preferred mixtures according to the present invention contain         ≦10% by weight of the compounds of the formulae P-1 to P-6.

-   j) Particularly preferred media contain one oder more compounds of     the formula II wherein X¹═X²═F.

-   k) Liquid-crystalline medium in which the proportion of the     compounds of the formula III in the mixture as a whole is from 0 to     50% by weight preferably from 3 to 50% by weight.

-   l) Liquid-crystalline medium which contains at least one indane     compound selected from the formulae In-1 to In-18:

-   -   Preferred LC mixtures contain at least 5-20% by weight of at         least one compound of the formula In-1 to In-18.     -   Particularly preferred media contain one or more compounds         selected from the group consisting of the compounds of the         formulae:

-   -   Particular preference is given to media which contain at least         one compound of the formula In-1a.

-   m) Liquid-crystalline medium which contains one, two, three, four or     more, preferably at least two compounds of the formula

-   n) Liquid-crystalline medium in which R¹ and R² in the formula I     preferably have independently of each other the following meanings:     straight-chain alkyl, vinyl, 1E-alkenyl or 3-alkenyl.     -   If R¹ denotes alkenyl, it is preferably CH₂═CH, CH₃—CH═CH,         C₃H₇—CH═CH, CH₂═CH—C₂H₄ or CH₃—CH═CH—C₂H₄.

-   o) Liquid-crystalline medium in which the proportion of compounds of     the formula I in the mixture as a whole is 1 to 30% by weight,     preferably at least 5% by weight, most preferably 5 to 15% by     weight, based on the total mixture.

-   p) Liquid-crystalline medium in which the proportion of compounds of     the formula II in the mixture as a whole is at least 30% by weight,     preferably at least 40%.

-   q) Preferred liquid-crystalline media according to the invention     contain one or more substances with a tetrahydronaphthyl or naphthyl     unit, such as, for example, the compounds of the formulae N-1 to     N-5.

-   -   in which R^(1N) and R^(2N) each, independently of one another,         have the meaning of R¹ in claim 1.

-   r) Preferred mixture concepts are given in the following.     -   LC mixture contains         -   at least one compound of the formula I, preferably at least             one compound of the formula Ia, and         -   at least one compound of the formula II and         -   at least one compound of the formula T-1.     -   LC mixture contains         -   at least one compound of the formula I, preferably at least             one compound of the formula Ia, and         -   at least one compound of the formula II, and         -   at least one compound of the formula B-1.     -   LC mixture contains         -   at least one compound of the formula I, preferably at least             one compound of the formula Ia, and         -   at least one compound of the formula II, and         -   at least one compound of the formula Z-15.     -   LC mixture contains         -   at least one compound of the formula I, preferably at least             one compound of the formula Ia, and         -   at least one compound of the formula II, and         -   at least one compound of the formula In-1 to In-18.     -   LC mixture contains         -   at least one compound of the formula I, preferably at least             one compound of the formula Ia, and         -   at least one compound of the formula IIj, Ilk and/or IIl.     -   LC mixture contains         -   at least one compound of the formula I, preferably at least             one compound of the formula Ia, and         -   at least one compound of the formula IIr.     -   LC mixture contains at least one compound of the formula with         the acronym CCOC-n-m listed in the following table.     -   LC mixture contains at least one compound of the formula with         the acronym CCPC-nm listed in the following table.     -   LC mixture contains at least one compound of the formula with         the acronym CH-nm listed in the following table.

The invention furthermore relates to an electro-optical display with active-matrix addressing based on the ECB effect, characterised in that it contains, as dielectric, a liquid-crystalline medium according to one of claims 1 to 9.

The liquid-crystalline medium preferably has a nematic phase range of at least 60 K and a flow viscosity ν₂₀ of at most 30 mm² s⁻¹ at 20° C.

The liquid-crystalline mixture according to the invention has a Δ∈ of about −0.5 to −8.0, in particular about −3.0 to −6.0, where Δ∈ denotes the dielectric anisotropy. The rotational viscosity γ₁ is preferably <150 mPa·s, in particular <140 mPa·s.

The birefringence Δn in the liquid-crystal mixture is generally from 0.07 to 0.18, preferably from 0.08 to 0.16, most preferably from 0.08 to 0.13.

The mixtures according to the invention are suitable for all VA-TFT applications, such as, for example, MVA, PVA, ASV and PS-VA. They are furthermore suitable for IPS, FFS and PALO applications with negative Δ∈.

The individual components of the formulae I, II and III of the liquid-crystal phases according to the invention are either known or their methods of preparation can easily be derived from the prior art by the person skilled in the relevant art since they are based on standard methods described in the literature.

The nematic liquid-crystal mixtures in the displays according to the invention generally comprise two components A and B, which themselves consist of one or more individual compounds.

Component A has significantly negative dielectric anisotropy and gives the nematic phase a dielectric anisotropy of ≦−0.3. It preferably comprises compounds of the formulae II.

The proportion of component A is preferably between 30 and 99%, in particular between 40 and 90%.

For component A, one (or more) individual compound(s) which has (have) a value of Δ∈ of ≦−0.8 is (are) preferably selected. This value must be more negative the smaller the proportion A in the mixture as a whole.

Component B has pronounced nematogeneity and a flow viscosity of not greater than 30 mm², s⁻¹, preferably not greater than 25 mm²·s⁻¹, at 20° C.

Particularly preferred individual compounds in component 13 are extremely low-viscosity nematic liquid crystals having a flow viscosity of not greater than 18 mm² s⁻¹, preferably not greater than 12 mm² s⁻¹, at 20° C.

Component B is monotropically or enantiotropically nematic, has no smectic phases and is able to prevent the occurrence of smectic phases down to very low temperatures in liquid-crystal mixtures. For example, if various materials of high nematogeneity are added to a smectic liquid-crystal mixture, the nematogeneity of these materials can be compared through the degree of suppression of smectic phases that is achieved.

A multiplicity of suitable materials is known to the person skilled in the art from the literature. Particular preference is given to compounds of the formulae I, II and III.

In addition, these liquid-crystal phases may also comprise more than 18 components, preferably 18 to 25 components.

The phases preferably comprise 4 to 15, in particular 5 to 12, compounds of the formulae I, II and optionally III.

Besides compounds of the formulae I, II and III, other constituents may also be present, for example in an amount of up to 45% of the mixture as a whole, but preferably up to 35%, in particular up to 10%.

The other constituents are preferably selected from nematic or nemato-genic substances, in particular known substances, from the classes of the azoxybenzenes, benzylideneanilines, biphenyls, terphenyls, phenyl or cyclohexyl benzoates, phenyl or cyclohexyl cyclohexanecarboxylates, phenylcyclohexanes, cyclohexylbiphenyls, cyclohexylcyclohexanes, cyclohexylnaphthalenes, 1,4-biscyclohexylbiphenyls or cyclohexyl-pyrimidines, phenyl- or cyclohexyldioxanes, optionally halogenated stilbenes, benzyl phenyl ethers, tolans and substituted cinnamic acids.

The most important compounds which are suitable as constituents of liquid-crystal phases of this type can be characterised by the formula IV

R⁹-L-G-E-R¹⁰  IV

in which L and E each denote a carbocyclic or heterocyclic ring system from the group formed by 1,4-disubstituted benzene and cyclohexane rings, 4,4′-disubstituted biphenyl, phenylcyclohexane and cyclohexylcyclo-hexane systems, 2,5-disubstituted pyrimidine and 1,3-dioxane rings, 2,6-disubstituted naphthalene, di- and tetrahydronaphthalene, quinazoline and tetrahydroquinazoline,

G is —CH═CH— —N(O)═N— —CH-CQ- —CH═N(O)— —C≡C— —CH₂—CH₂— —CO—O— —CH₂—O— —CO—S— —CH₂—S— —CH═N— —COO-Phe-COO— —CF₂O— —CF═CF— —OCF₂ —OCH₂— —(CH₂)₄— —(CH₂)₃O— or a C—C single bond, Q denotes halogen, preferably chlorine, or —CN, and R⁹ and R¹⁰ each denote alkyl, alkenyl, alkoxy, alkanoyloxy or alkoxycar-bonyloxy having up to 18, preferably up to 8 carbon atoms, or one of these radicals alternatively denotes CN, NC, NO₂, NCS, CF₃, OCF₃, F, Cl or Br.

In most of these compounds, R⁹ and R¹⁰ are different from one another, one of these radicals usually being an alkyl or alkoxy group. Other variants of the proposed substituents are common. Many such substances or also mixtures thereof are also commercially available. All these substances can be prepared by methods known from the literature.

It goes without saying for the person skilled in the art that the VA, IPS or PALC mixture according to the invention may also comprise compounds in which, for example, H, N, O, Cl and F have been replaced by the corresponding isotopes.

The construction of the liquid-crystal displays according to the invention corresponds to the usual geometry, as described, for example, in EP-A 0 240 379.

The following examples are intended to explain the invention without limiting it. Above and below, percentages are percent by weight based on the total mixture; all temperatures are indicated in degrees Celsius.

Besides the compounds of the formulae I and II, the mixtures according to the invention preferably comprise one or more of the compounds shown below.

The following abbreviations are used:

(n and m=1-6; z=1-6; m(O)m denotes n-m or n-Om)

The liquid-crystal mixtures which can be used in accordance with the invention are prepared in a manner which is conventional per se. In general, the desired amount of the components used in lesser amount is dissolved in the components making up the principal constituent, advantageously at elevated temperature. It is also possible to mix solutions of the components in an organic solvent, for example in acetone, chloroform or methanol, and to remove the solvent again, for example by distillation, after mixing.

The dielectrics may also comprise further additives known to the person skilled in the art and described in the literature, such as, for example, UV absorbers, nanoparticles, nanobeeds, microparticles, antioxidants and free-radical scavengers. For example, 0-15% of pleochroic dyes, stabilisers or chiral dopants may be added.

For example, 0-15% of pleochroic dyes may be added, furthermore conductive salts, preferably ethyldimethyldodecylammonium 4-hexoxybenzoate, tetrabutylammonium tetraphenylboranate or complex salts of crown ethers (cf., for example, Haller at al., Mol. Cryst. Liq. Cryst. Volume 24, pages 249-258 (1973)) in order to improve the conductivity or substances may be added in order to modify the dielectric anisotropy, the viscosity and/or the alignment of the nematic phases. Substances of this type are described, for example, in DE-A 22 09 127, 22 40 864, 23 21 632, 23 38 281, 24 50 088, 26 37 430 and 28 53 728.

Table A shows for example possible dopants which can be added to the mixtures according to the invention. If the mixtures according to the invention comprise a dopant, it is generally added in amounts of 0.01 to 4.0% by weight, preferably 0.1 to 1.0% by weight.

TABLE A

  C 15

  CB 15

  CM 21

  R/S-811

  CM 44

  CM 45

  CM 47

  CN

  R/S-1011

  R/S-2011

  R/S-3011

  R/S-4011

  R/S-5011

Stabilisers which can be added, for example, to the mixtures according to the invention are shown below in Table B.

TABLE B

(n = 1-12)

The following examples are intended to explain the invention without limiting it. Above and below,

-   V_(o) denotes the threshold voltage, capacitive [V] at 20° C. -   Δn denotes the optical anisotropy measured at 20° C. and 589 nm -   Δ∈ denotes the dielectric anisotropy at 20° C. and 1 kHz -   cp. denotes the clearing point [° C.] -   γ₁ denotes the rotational viscosity measured at 20° C. [mPa·s] -   LTS denotes the low temperature stability, determined in test cells

For the purposes of the present invention, all concentrations are, unless explicitly stated otherwise, indicated in percent by weight and relate to the corresponding mixture or mixture component. All physical properties are and have been determined in accordance with “Merck Liquid Crystals, Physical Properties of Liquid Crystals”, Status November 1997, Merck KGaA, Germany, and apply to a temperature of 20° C., unless explicitly stated otherwise. The rotational viscosity is determined by the rotating permanent magnet method and the flow viscosity in a modified Ubbelohde viscometer.

The display used for measurement of the threshold voltage has two plane-parallel outer plates at a separation of 20 μm and electrode layers with overlying alignment layers of SE-1211 (Nissan Chemicals) on the insides of the outer plates, which effect a homeotropic alignment of the liquid crystals.

The following examples are intended to explain the invention without restricting it.

MIXTURE EXAMPLES Example 1

A liquid crystal mixture containing

CY-3-O4 32.00% cp. [° C.]: 100.8 CY-5-O2 6.00% Δn [589 nm, 20° C.]: 0.1504 CCY-3-O2 7.00% CCY-4-O2 7.00% CCY-3-O3 2.00% CCY-3-1 4.00% PYP-2-3 10.00% PYP-2-4 10.00% BCH-32 7.00% CPGP-5-3 6.00% CPGP-5-2 6.00% CPGP-4-3 3.00%

Example 2

A liquid crystal mixture containing

CY-3-O4 32.00% cp. [° C.]: 101.5 CY-5-O2 6.00% Δn [589 nm, 20° C.]: 0.150 CCY-3-O2 7.00% Δε [1 kHz, 20° C.]: −4.0 CCY-1-O2 7.00% K₁ [20° C.]: 15.1 CCY-3-O3 4.00% K₃ [20° C.]: 17.0 PYP-2-3 10.00% K₃/K₁ [20° C.]: 1.13 PYP-2-4 10.00% V₀ [20° C.]: 2.17 V BCH-32 7.00% CPGP-5-3 6.00% CPGP-5-2 6.00% CPGP-1-3 3.00% CCP-V-1 2.00%

Example 3

A liquid crystal mixture containing

CY-3-O4 30.00% cp. [° C.]: 98.4 CY-5-O2 4.00% Δn [589 nm, 20° C.]: 0.1631 CCY-3-O2 5.00% Δε [1 kHz, 20° C.]: −4.0 CCY-4-O2 8.00% K₁ [20° C.]: 15.3 CCY-3-O3 8.00% K₃ [20° C.]: 17.2 PYP-2-3 10.00% K₃/K₁ [20° C.]: 1.12 PYP-2-4 10.00% V₀ [20° C.]: 2.19 V PGP-2-3 14.00% CPGP-5-3 10.00%

Example 4

A liquid crystal mixture containing

CY-3-O4 19.00% cp. [° C.]: 113 CY-5-O4 18.00% Δn [589 nm, 20° C.]: 0.1072 CCY-3-O2 6.00% Δε [1 kHz, 20° C.]: −5.6 CCY-3-O3 6.00% CCY-4-O2 6.00% CCY-5-O2 6.00% CPY-2-O2 9.00% CPY-3-O2 9.00% CH-43 3.00% CH-45 3.00% CCOC-3-3 2.00% CCOC-4-3 2.00% CCOC-3-5 2.00% CCPC-33 3.00% CCPC-34 3.00% CPGP-5-3 3.00%

Example 5

A liquid crystal mixture containing

CY-3-O4 26.00% cp. [° C.]: 85.9 CY-3-O2 10.00% Δn [589 nm, 20° C.]: 0.1117 CCY-3-O2 7.00% Δε [1 kHz, 20° C.]: −4.7 CCY-3-O3 7.00% K₁ [20° C.]: 14.7 CCY-4-O2 6.00% K₃ [20° C.]: 16.4 CCY-5-O2 6.00% K₃/K₁ [20° C.]: 1.11 CCY-2-1 9.00% V₀ [20° C.]: 1.98 V CCY-3-1 8.00% PGP-2-3 10.00% CPGP-5-2 3.00% CC-3-V1 8.00%

Example 6

A liquid crystal mixture containing

CY-3-O4 28.00% cp. [° C.]: 85.2 CCY-3-O2 7.00% Δn [589 nm, 20° C.]: 0.1134 CCY-3-O3 6.00% Δε [1 kHz, 20° C.]: −4.8 CCY-4-O2 6.00% K₁ [20° C.]: 14.3 CCY-5-O2 6.00% K₃ [20° C.]: 14.3 CCY-3-1 8.00% K₃/K₁ [20° C.]: 1.00 PGP-2-3 13.00% V₀ [20° C.]: 1.84 V CPGP-5-2 4.00% CC-4-V 10.00% CK-3-F 4.00% CK-4-F 4.00% CK-5-F 4.00%

Example 7

A liquid crystal mixture containing

CY-3-O4 28.00% cp. [° C.]: 83.3 CY-5-04 15.00% Δn [589 nm, 20° C.]: 0.1107 CCY-3-O2 8.00% Δε [1 kHz, 20° C.]: −4.0 CCY-3-O3 8.00% K₁ [20° C.]: 12.6 CCY-4-O2 8.00% K₃ [20° C.]: 14.3 CPGP-5-2 7.00% K₃/K₁ [20° C.]: 1.14 CPGP-5-3 6.00% V₀ [20° C.]: 2.00 V CC-4-V 14.00% PGP-2-3 6.00%

Example 8

A liquid crystal mixture containing

CY-3-O4 25.00% cp. [° C.]: 87.5 CCY-3-O2 7.00% Δn [589 nm, 20° C.]: 0.1121 CCY-3-O3 7.00% Δε [1 kHz, 20° C.]: −4.0 CCY-4-O2 7.00% K₁ [20° C.]: 13.1 CCY-3-1 7.00% K₃ [20° C.]: 14.5 PGP-2-3 11.00% K₃/K₁ [20° C.]: 1.11 CPGP-5-2 8.00% V₀ [20° C.]: 2.00 V CC-4-V 16.00% CK-3-F 4.00% CK-4-F 4.00% CK-5-F 4.00%

Example 9

A liquid crystal mixture containing

CY-3-O4 21.00% cp. [° C.]: 87.6 CY-5-O4 13.00% Δn [589 nm, 20° C.]: 0.1088 CCY-3-O2 7.00% Δε [1 kHz, 20° C.]: −4.9 CCY-3-O3 7.00% K₁ [20° C.]: 15.3 CCY-4-O2 6.00% K₃ [20° C.]: 16.1 CPY-3-O2 11.00% K₃/K₁ [20° C.]: 1.05 CCY-2-1 7.00% V₀ [20° C.]: 1.93 V CCY-3-1 7.00% PYP-2-3 5.50% CPGP-5-2 3.50% CC-3-V1 5.00% CC-5-V 7.00%

Example 10

A liquid crystal mixture containing

CY-3-O4 21.00% cp. [° C.]: 87.5 CY-5-O4 14.00% Δn [589 nm, 20° C.]: 0.1092 CCY-3-O2 7.00% Δε [1 kHz, 20° C.]: −4.8 CCY-3-O3 6.00% K₁ [20° C.]: 15.0 CCY-4-O2 5.50% K₃ [20° C.]: 16.1 CPY-3-O2 11.00% K₃/K₁ [20° C.]: 1.08 CCY-2-1 7.00% V₀ [20° C.]: 1.95 V CCY-3-1 7.00% PYP-2-3 5.00% CPGP-5-2 4.50% CC-3-V1 5.50% CC-5-V 6.50%

Example 11

A liquid crystal mixture containing

CY-3-O4 24.50% cp. [° C.]: 88.5 CCY-3-O2 8.00% Δn [589 nm, 20° C.]: 0.1098 CCY-3-O3 8.00% Δε [1 kHz, 20° C.]: −4.2 CCY-4-O2 8.00% K₁ [20° C.]: 13.2 CCY-3-1 7.00% K₃ [20° C.]: 14.7 PGP-2-3 10.00% K₃/K₁ [20° C.]: 1.11 CPGP-5-2 7.00% V₀ [20° C.]: 1.97 V CC-4-V 15.50% CK-3-F 4.00% CK-4-F 4.00% CK-5-F 4.00%

Example 12

A liquid crystal mixture containing

CY-3-O4 25.00% cp. [° C.]: 88.8 CCY-3-O2 7.00% Δn [589 nm, 20° C.]: 0.1099 CCY-3-O3 7.00% Δε [1 kHz, 20° C.]: −4.4 CCY-4-O2 7.00% K₁ [20° C.]: 14.0 CCY-5-O2 4.00% K₃ [20° C.]: 14.5 CCY-3-1 6.00% K₃/K₁ [20° C.]: 1.04 PGP-2-3 7.00% V₀ [20° C.]: 1.94 V PGP-2-4 3.00% CPGP-5-2 7.00% CC-4-V 15.00% CK-3-F 4.00% CK-4-F 4.00% CK-5-F 4.00%

Example 13

A liquid crystal mixture containing

CY-3-O4 25.00% cp. [° C.]: 90.4 CCY-3-O2 7.00% Δn [589 nm, 20° C.]: 0.1090 CCY-3-O3 6.00% Δε [1 kHz, 20° C.]: −4.5 CCY-4-O2 6.00% K₁ [20° C.]: 14.0 CPY-3-O2 12.00% K₃ [20° C.]: 15.4 PGP-2-3 4.00% K₃/K₁ [20° C.]: 1.10 CPGP-5-2 6.00% V₀ [20° C.]: 1.96 V CCP-V-1 7.00% γ₁ [mPa · s, 20°]: 187 CC-4-V 16.00% LTS Bulk [−30° C.] >1000 h CK-3-F 4.00% CK-4-F 3.00% CK-5-F 4.00%

Example 14

A liquid crystal mixture containing

CY-3-O4 29.50% cp. [° C.]: 100.8 CCY-2-1 10.50% Δn [589 nm, 20° C.]: 0.1329 CCY-3-1 10.00% Δε [1 kHz, 20° C.]: −3.8 CCY-3-O2 6.00% K₁ [20° C.]: 15.6 CCY-4-O2 7.00% K₃ [20° C.]: 16.6 CCY-3-O3 4.00% K₃/K₁ [20° C.]: 1.06 PYP-2-3 7.00% V₀ [20° C.]: 2.18 V PYP-2-4 6.00% LTS Bulk [−20° C.] >1000 h BCH-32 14.00% CPGP-5-3 3.00% CPGP-5-2 3.00%

Example 15

A liquid crystal mixture containing

CY-3-O4 32.00% cp. [° C.]: 100.6 CY-5-O2 11.00% Δn [589 nm, 20° C.]: 0.1462 CCY-3-O3 10.00% Δε [1 kHz, 20° C.]: −4.4 CCY-5-O2 10.00% K₁ [20° C.]: 14.7 PYP-2-3 8.00% K₃ [20° C.]: 17.3 PYP-2-4 8.00% K₃/K₁ [20° C.]: 1.18 BCH-32 2.00% V₀ [20° C.]: 2.09 V CPGP-5-3 7.00% CPGP-5-2 7.00% CPGP-4-3 5.00%

Example 16

A liquid crystal mixture containing

CY-3-O4 32.00% cp. [° C.]: 100.8 CY-5-O2 7.00% Δn [589 nm, 20° C.]: 0.1303 CCY-2-1 8.00% Δε [1 kHz, 20° C.]: −4.3 CCY-3-O2 8.00% K₁ [20° C.]: 15.0 CCY-4-O2 7.00% K₃ [20° C.]: 17.3 CCY-3-O3 7.00% K₃/K₁ [20° C.]: 1.15 PYP-2-3 6.00% V₀ [20° C.]: 2.12 V BCH-32 13.00% LTS Bulk [−20° C.] >1000 h CPGP-5-2 6.00% CPGP-5-3 6.00%

Example 17

A liquid crystal mixture containing

CY-3-O4 32.00% cp. [° C.]: 100.7 CY-3-O4 29.00% Δn [589 nm, 20° C.]: 0.1320 CY-5-O2 11.00% Δε [1 kHz, 20° C.]: −4.0 CCY-2-1 7.00% K₁ [20° C.]: 16.1 CCY-3-O2 8.00% K₃ [20° C.]: 17.3 CCY-4-O2 7.00% K₃/K₁ [20° C.]: 1.07 CCY-3-O3 4.50% V₀ [20° C.]: 2.16 V PYP-2-3 6.00% LTS Bulk [−20° C.] >1000 h BCH-32 15.50% CPGP-5-2 6.00% CPGP-5-3 6.00%

Example 18

A liquid crystal mixture containing

CY-3-O4 32.00% cp. [° C.]: 104.7 CY-5-O2 6.00% Δn [589 nm, 20° C.]: 0.1360 CCY-2-1 8.00% K₁ [20° C.]: 16.7 CCY-3-1 3.00% K₃ [20° C.]: 17.7 CCY-3-O2 7.00% K₃/K₁ [20° C.]: 1.06 CCY-4-O2 7.00% V₀ [20° C.]: 2.25 V CCY-3-O3 5.00% LTS Bulk [−20° C.] >1000 h PYP-2-3 8.00% BCH-32 10.00% CPGP-5-2 6.00% CPGP-5-3 6.00% CPGP-4-3 2.00%

Example 19

A liquid crystal mixture containing

CY-3-O4 29.00% cp. [° C.]: 103.8 CCY-2-1 10.00% Δn [589 nm, 20° C.]: 0.1331 CCY-3-1 10.00% K₁ [20° C.]: 16.7 CCY-3-O2 7.00% K₃ [20° C.]: 17.2 CCY-4-O2 7.00% K₃/K₁ [20° C.]: 1.03 CCY-3-O3 6.00% V₀ [20° C.]: 2.16 V PYP-2-3 8.00% LTS Bulk [−20° C.] >1000 h PYP-2-4 5.00% BCH-32 11.00% CPGP-5-3 3.00% CPGP-5-2 3.00% CPGP-4-3 1.00%

Example 20

A liquid crystal mixture containing

CY-3-O2 7.00% cp. [° C.]: 84.5 CY-3-O4 11.00% Δn [589 nm, 20° C.]: 0.1107 CCY-3-O2 3.00% CCY-3-O3 7.00% CCY-4-O2 8.00% CPY-2-O2 8.00% CPY-3-O2 8.00% CC-3-V 20.50% CC-5-V 7.00% CC-3-V1 6.00% CPGP-5-2 1.50% PYP-2-3 9.00% PYP-2-4 4.00% 

1. A liquid crystalline medium containing at least one compound of formula I, at least one compound of formula II, and at least one compound of formula IIIe and/or IIIf

wherein R¹ to R⁴ are each independently alkyl or alkoxy with 1 to 8 C atoms, wherein one or more CH₂-groups are optionally replaced by —CH═CH—, —CF₂O or —O— in a way that —O— atoms are not linked directly to one another,

X¹ and X² are each independently F, Cl or CF₃, Z¹ and Z² are each independently a single bond, —CH₂CH₂—, —CH₂O—, —OCH₂—, —CF₂O—, —OCF₂—, —COO— m is 0 or 1, alkyl denotes a straight-chain alkyl radical having 1-6 C atoms, and alkenyl and alkenyl* each, independently of one another, denote a straight-chain alkenyl radical having 2-6 C atoms.
 2. A liquid crystalline medium according to claim 1, comprising one or more compounds of the following formulae

wherein alkyl and alkyl* independently for each other denote C₁₋₆-alkyl and alkenyl and alkenyl* independently for each other denote C₂₋₆-alkenyl.
 3. A liquid crystalline medium according to claim 2, comprising one or more compounds of formula Ia.
 4. A liquid crystalline medium according to claim 1, comprising one or more compounds of the following formulae IIa to IIr,

wherein alkyl and alkyl* independently for each other denote C₁₋₆-alkyl, alkenyl denotes C₂₋₆-alkenyl, and X¹ and X² are each independently F, Cl or CF₃.
 5. A liquid crystalline medium according to claim 1, further comprising one or more compounds of formula III, which are not a compound of formula IIIe or IIIf

wherein R⁵ and R⁶ are independently of each other alkyl or alkoxy with 1 to 8 C atoms wherein one or more CH₂-groups are optionally replaced by —CH═CH—,

are independently of each other

n is 0 or
 1. 6. A liquid crystalline medium according to claim 5, comprising one or more compounds of formulae IIIa to IIId and IIIg to IIIn

wherein alkyl and alkyl* each, independently of one another, denote a straight-chain alkyl radical having 1-6 C atoms, and alkenyl denotes a straight-chain alkenyl radical having 2-6 C atoms.
 7. A liquid crystalline medium according to claim 1, wherein the proportion of the compounds of formula I in the liquid crystalline medium as a whole is 1 to 30% by weight.
 8. A liquid crystalline medium according to claim 1, wherein the proportion of the compound of formula II in the liquid crystalline medium as a whole is at least 30% by weight.
 9. A liquid crystalline medium according to claim 5, wherein the proportion of the compound of formula III in the liquid crystalline medium as a whole is 3 to 50% by weight.
 10. A method for achieving an electrooptical effect, comprising addressing a liquid crystalline medium according to claim
 1. 11. An electrooptical liquid crystal display containing a liquid crystalline medium according to claim
 1. 12. An electrooptical display according to claim 11, which it has active matrix addressing and is based on the ECB, VA, ASV, PS-VA, MVA, FFS or PALC mode.
 13. A liquid crystalline medium according to claim 1, wherein the at least one compound of formula IIIe and/or IIIf are selected from the group consisting of


14. A liquid crystalline medium according to claim 1, which contains >30% by weight at least one compound of formula IIIe and/or IIIf, which are selected from the group consisting of


15. A liquid crystalline medium according to claim 1, which contains >35% by weight at least one compound of formula IIIe and/or IIIf, which are selected from the group consisting of


16. A liquid crystalline medium according to claim 1, which contains >30% by weight at least one compound of formula IIIe and/or IIIf.
 17. A liquid crystalline medium according to claim 1, which contains >35% by weight at least one compound of formula IIIe and/or IIIf.
 18. A liquid crystalline medium according to claim 13, which contains >30% by weight at least one compound of formula IIIe and/or IIIf.
 19. A liquid crystalline medium according to claim 13, which contains >35% by weight at least one compound of formula IIIe and/or IIIf. 